Nkeọgwụgwọ okpomọkụusoro nke ígwè na-ezo aka kpọmkwem kpo oku, mkpuchi na jụrụ usoro parameters nke ígwè n'oge okpomọkụ ọgwụgwọ, nke na-formed dị ka structural mgbanwe iwu nke ígwè n'oge kpo oku na jụrụ.
Nhazi
Dị ka usoro kpo oku na oyi na ihe dị iche iche na ihe onwunwe nwetara, usoro ọgwụgwọ okpomọkụ nke ígwè nwere ike kewaa n'ime:
(1) Ọgwụgwọ okpomọkụ nkịtị (na-akụda mmụọ, na-edozi ahụ, na-emenyụ ọkụ na iwe ọkụ)
(2) Ngwọta ikpo ọkụ dị n'elu (nkwụsị elu na ọgwụgwọ okpomọkụ kemịkal, wdg)
(3) ọgwụgwọ okpomọkụ pụrụ iche (ngwọ ọrịa okpomọkụ nrụrụ, ọgwụgwọ ọkụ magnetik, wdg).
Dị ka ọnọdụ na ọrụ nke ọgwụgwọ okpomọkụ na usoro nhazi nke mmepụta akụkụ, enwere ike kewaa ọgwụgwọ okpomọkụ n'ime:
(1) Ọgwụgwọ okpomọkụ nke mbido, tumadi nfụkasị ahụ, ime ka ọ dị mma, wdg.
(2) Ọgwụgwụ okpomọkụ ikpeazụ, tumadi quenching, tempering, wdg.
Annealing na normalizing nke ígwè
Na-ewe iwe
Usoro ọgwụgwọ okpomọkụ nke kpo oku ígwè nwere ihe owuwu na-esi na ọnọdụ nha anya gaa na okpomọkụ kwesịrị ekwesị,
na-ekpuchi ya ruo oge ụfọdụ, wee jiri nwayọọ nwayọọ mee ka ọ dị jụụ iji nweta ihe owuwu dị nso na steeti nhata ka a na-akpọ annealing.
Ebumnuche
Wepụ kristal kọlụm na-enweghị isi na kristal nha nhata, nụchaa ọka, belata ike isi ike, melite arụmọrụ ịkpụ, ma mee ka usoro ahụ bụrụ otu.
Nhazi
E nwere ọtụtụ ụdị usoro ịhịa aka nchara, nke nwere ike kewaa ụzọ abụọ dịka okpomọkụ okpomọkụ si dị:
1. Ngbanwe nke oge recrystallization annealing, gụnyere mgbakasị ahụ zuru oke, mgbakasị ahụ ezughị ezu,
spheroidizing annealing na mgbasa annealing.
2. Annealing n'okpuru okpomọkụ dị oke egwu, gụnyere recrystallization annealing na annealing enyemaka nchekasị.
Enwere ike iwere Normalizing dị ka ụdị pụrụ iche nke mgbakasị ahụ, na usoro jụrụ oyi bụ ikuku jụrụ oyi.
1 Ntugharị zuru oke
Annealing zuru ezu bụ usoro ọgwụgwọ okpomọkụ nke na-ekpo ọkụ nchara na 30-50 ℃ n'elu AC3 okpomọkụ, na-edebe okpomọkụ ruo oge zuru ezu, na-eme ka usoro ahụ dịkwuo mma, wee jiri nwayọọ nwayọọ mee ka ọ dị jụụ na ọkụ iji nweta usoro ọgwụgwọ okpomọkụ dị nso na nhazi nha nhata.
Ebumnuche bụ iji nụchaa ọka, mee ka ihe owuwu ahụ bụrụ otu, wepụ nchekasị dị n'ime na mmejọ nhazi na-ekpo ọkụ, belata ike siri ike, ma melite arụmọrụ ịkpụ na arụ ọrụ nrụrụ plastik oyi.
A na-emezigharị ihe owuwu ahụ, na-eme ka ọka na-eme ka a nụchaa, ihe owuwu ahụ na-adị otu, wee kpochapụ ihe owuwu Widmanstätten na ihe owuwu banded. N'ihi na forgings na Rolling akụkụ, zuru annealing na-ahaziri mgbe workpiece na-ekpo ọkụ forged na-ekpo ọkụ akpọrepu, na tupu ịcha: n'ihi na welded akụkụ ma ọ bụ nkedo, ọ na-emekarị ndokwa mgbe ịgbado ọkụ na agbapụta (ma ọ bụ mgbe mgbasa annealing).
Ọkụ ọkụ na oge okpomọkụ na-adịkarị 20-30 ℃ n'elu Ac3. The annealing njide oge na-adabere ọ bụghị nanị na oge achọrọ maka workpiece ọkụ site (ya bụ, isi nke workpiece ruru okpomọkụ a chọrọ), kamakwa na oge achọrọ maka nhazi mgbanwe. Oge na-ejide oge zuru ezu na-ejikọta kemịkalụ kemịkalụ nke ígwè, ọdịdị na nha nke workpiece, ụdị ngwá ọrụ ọkụ ọkụ, ọnụ ọgụgụ nke ọkụ ọkụ na usoro nke loading. A na-agbakọkarị oge kpo oku dabere na ọkpụrụkpụ dị irè nke workpiece.
Usoro jụrụ oyi ọkụ dị jụụ,ihe nkedo carbon ígwè<200 ℃/h, obereihe nkedo alloy ígwè<100 ℃ / h, elu alloy ígwè <50 ℃ / h. Igwe ọkụ ọkụ <600 ℃.
Nhazi:Lamellar pearlite
Usoro mgbakasị nke nkedo ígwè carbon na ike siri ike mgbe emechara ya
| Ọdịnaya Carbon (%) | Annealing okpomọkụ | nchekwa okpomọkụ | Ụzọ jụrụ oyi | Isi ike (HB) | |
| Ọkpụrụkpụ mgbidi nke nkedo / mm | oge / elekere (s) | ||||
| 0.10-0.20 | 910-880 | 30 | 1 | Igwe ọkụ na-ekpo ọkụ ruo 620 ℃ - ikuku jụrụ oyi | 115-143 |
| 0.20-0.30 | 880-850 | 30 | 1 | Igwe ọkụ na-ekpo ọkụ ruo 620 ℃ - ikuku jụrụ oyi | 133-156 |
| 0.30-0.40 | 850-820 | 30 | Kwa 30 mm na-abawanye, tinye 1 hour | Igwe ọkụ na-ekpo ọkụ ruo 620 ℃ - ikuku jụrụ oyi | 143-178 |
| 0.40-0.50 | 820-800 | 30 | Kwa 30 mm na-abawanye, tinye 1 hour | Igwe ọkụ na-ekpo ọkụ ruo 620 ℃ - ikuku jụrụ oyi | 156-217 |
| 0.50-0.60 | 800-780 | 30 | Kwa 30 mm na-abawanye, tinye 1 hour | Igwe ọkụ na-ekpo ọkụ ruo 620 ℃ - ikuku jụrụ oyi | 187-230 |
Oge nzipu: Dec-13-2024