Ngwọta okpomọkụ nke nkedo ígwè na-adabere na eserese nke Fe-Fe3C iji chịkwaa microstructure nke ihe nkedo ígwè iji nweta ọrụ achọrọ. Ọgwụgwọ okpomọkụ bụ otu n'ime usoro dị mkpa na mmepụta nke nkedo ígwè. Ogo na mmetụta nke ọgwụgwọ okpomọkụ na-emetụta kpọmkwem na arụmọrụ ikpeazụ nke nkedo ígwè.
Usoro ihe nkedo nke nkedo ígwè na-adabere na nhazi kemịkalụ na usoro siri ike. N'ozuzu, enwere oke dendrite dị oke njọ, usoro na-enweghị isi na ọka na-enweghị isi. Ya mere, ihe nkedo ígwè n'ozuzu kwesịrị ka a gwọọ ya iji kpochapụ ma ọ bụ ibelata mmetụta nke nsogbu ndị a dị n'elu, iji meziwanye ihe eji arụ ọrụ nke nkedo ígwè. Tụkwasị na nke ahụ, n'ihi ọdịiche dị na nhazi na mgbidi nke ihe nkedo ígwè, akụkụ dị iche iche nke otu ihe nkedo ahụ nwere ụdị nhazi dị iche iche ma na-emepụta nrụgide dị n'ime ụlọ dị ukwuu. Ya mere, ihe nkedo ígwè (karịsịa ihe nkedo ígwè) kwesịrị ịnapụta n'ozuzu ya na ọnọdụ okpomọkụ.
1. Njirimara nke ọgwụgwọ okpomọkụ nke nkedo ígwè
1) N'ime usoro ihe nkedo nke nkedo ígwè, a na-enwekarị dendrites na-enweghị isi na nkewa. N'oge ọgwụgwọ okpomọkụ, oge ikpo ọkụ kwesịrị ịdị elu karịa nke akụkụ ígwè na-emepụta ihe nke otu ihe ahụ. N'otu oge ahụ, ọ dị mkpa ịgbatị oge njide nke nnabata nke ọma.
2) N'ihi oke nkewa nke ihe nkedo dị ka ihe nkedo nke ụfọdụ ihe nkedo ígwè, iji kpochapụ mmetụta ya na njirimara ikpeazụ nke ihe nkedo ahụ, ekwesịrị ịme usoro iji homogenize n'oge ọgwụgwọ okpomọkụ.
3) Maka ihe nkedo ígwè nwere ọdịdị dị mgbagwoju anya na nnukwu mgbidi dị iche iche, a ghaghị ịtụle mmetụta nke akụkụ na nkedo nrụgide n'oge ọgwụgwọ okpomọkụ.
4) Mgbe a na-eme ọgwụgwọ okpomọkụ na nkedo ígwè, ọ ghaghị ịbụ ihe ezi uche dị na ya dabere na njirimara nhazi ya ma gbalịa izere nrụrụ nke nkedo.
2. Isi ihe na-akpata usoro ọgwụgwọ okpomọkụ nke nkedo ígwè
Ngwọta okpomọkụ nke nkedo ígwè nwere usoro atọ: kpo oku, nchekwa ọkụ, na oyi. Mkpebi nke usoro usoro kwesịrị ịdabere n'ebumnobi nke ijide n'aka àgwà ngwaahịa na ịchekwa ego.
1) kpo oku
Igwe ọkụ bụ usoro kachasị ike na-eri na usoro ọgwụgwọ okpomọkụ. Ihe ndị bụ isi teknụzụ nke usoro kpo oku bụ ịhọrọ usoro kpo oku kwesịrị ekwesị, ọsọ ọkụ na usoro ịgba ụgwọ.
(1) Usoro ikpo ọkụ. Ụzọ kpo oku nke ihe nkedo nchara gụnyere tumadi kpo oku, kpo oku ịsa nnu na kpo oku induction. Ụkpụrụ nhọrọ nke usoro kpo oku bụ ngwa ngwa na otu, dị mfe ịchịkwa, arụmọrụ dị elu na ọnụ ala. Mgbe a na-ekpo ọkụ, ebe a na-emepụta ihe na-atụlekarị nha nhazi, ihe mejupụtara kemịkalụ, usoro ọgwụgwọ okpomọkụ na ihe dị mma chọrọ nke nkedo.
(2) Ọsọ ọkụ. Maka ihe nkedo nchara n'ozuzu, ọkụ ọkụ ọkụ nwere ike ọ gaghị ejedebe, na ike kachasị nke ọkụ ọkụ na-eji maka ikpo ọkụ. Ojiji nke ọkụ ọkụ na-ekpo ọkụ nwere ike belata oge ikpo ọkụ na usoro mmepụta. N'ezie, n'okpuru ọnọdụ nke ikpo ọkụ ngwa ngwa, ọ dịghị ihe doro anya okpomọkụ hysteresis n'etiti elu nke nkedo na isi. Kpọọ ngwa ngwa ga-eme ka nrụpụta nrụpụta belata, ịba ụba ike oriri, yana oke oxidation na decarburization n'elu nkedo ahụ. Otú ọ dị, maka ụfọdụ ihe nkedo nwere ọdịdị dị mgbagwoju anya na ihe owuwu, nnukwu mgbidi mgbidi, na nnukwu nrụgide okpomọkụ n'oge usoro ikpo ọkụ, a ghaghị ịchịkwa ọsọ ọkụ ọkụ. N'ozuzu, enwere ike iji obere okpomọkụ na ọkụ na-ekpo ọkụ (n'okpuru 600 Celsius) ma ọ bụ ịnọrọ na okpomọkụ dị ala ma ọ bụ nke ọkara, mgbe ahụ enwere ike iji kpo oku ngwa ngwa na mpaghara okpomọkụ dị elu.
(3) Ụzọ ntinye. Ụkpụrụ nke a ga-etinye nkedo ígwè n'ime ọkụ bụ iji ohere dị irè mee ihe n'ụzọ zuru ezu, hụ na ikpo ọkụ otu na-etinye ihe nkedo ahụ iji mebie.
2) mkpuchi
Ekwesịrị ịhọrọ okpomọkụ na-ejide maka austenitization nke nkedo ígwè dị ka ihe mejupụtara kemịkalụ nke ihe nkedo na ihe ndị achọrọ. Okpomọkụ ejidere na-adịkarị elu karịa (ihe dịka 20 Celsius) karịa imepụta akụkụ nchara nke otu ihe. Maka nkedo ígwè eutectoid, ekwesịrị ijide n'aka na enwere ike itinye carbide ngwa ngwa n'ime austenite, nakwa na austenite nwere ike ịnọgide na-enwe ezigbo ọka.
Ekwesịrị ịtụle ihe abụọ maka oge nchekwa okpomọkụ nke ihe nkedo ígwè: ihe mbụ bụ ime ka okpomọkụ nke ihe nkedo na isi edozi, na nke abụọ bụ iji hụ na nhazi nke nhazi ahụ. Ya mere, oge njide na-adabere na conductivity thermal nke nkedo, mgbidi mgbidi nke ngalaba na ihe ndị na-emepụta ihe. N'ikwu okwu n'ozuzu, nkedo nchara na-achọ ogologo oge karịa nkedo ígwè carbon. Mgbidi mgbidi nke nkedo na-abụkarị ihe ndabere maka ịgbakọ oge njide. Maka njide oge ọgwụgwọ iwe ọkụ na ọgwụgwọ ịka nká, ihe ndị dị ka nzube nke ọgwụgwọ okpomọkụ, njide okpomọkụ na ọnụego mgbasa ozi kwesịrị ịtụle.
3) jụrụ oyi
Enwere ike ime ka ihe nkedo ígwè dị jụụ na ọsọ ọsọ dị iche iche mgbe nchekwa ọkụ gasịrị, iji mechaa mgbanwe metallographic, nweta nhazi metallographic achọrọ ma nweta ihe ngosi arụmọrụ akọwapụtara. N'ikwu okwu n'ozuzu, ịba ụba ọnụego jụrụ oyi nwere ike inye aka nweta nhazi dị mma na nụchaa ọka, si otú ahụ na-emeziwanye ihe eji arụ ọrụ nke nkedo ahụ. Otú ọ dị, ọ bụrụ na ọnụego jụrụ oyi na-adị ngwa ngwa, ọ dị mfe ịkpata nchekasị ka ukwuu na nkedo. Nke a nwere ike ịkpata nrụrụ ma ọ bụ mgbawa nke nkedo nwere usoro dị mgbagwoju anya.
Igwe nju oyi maka ọgwụgwọ okpomọkụ nke ihe nkedo ígwè na-agụnyekarị ikuku, mmanụ, mmiri, mmiri nnu na nnu gbazere.
3. Usoro ọgwụgwọ okpomọkụ nke nkedo ígwè
Dị ka usoro ikpo ọkụ dị iche iche si dị, ijide oge na ọnọdụ jụrụ oyi, usoro ọgwụgwọ okpomọkụ nke ihe nkedo ígwè na-agụnye ịkachasị ahụ, normalizing, quenching, tempering, ọgwụgwọ ngwọta, mmiri ozuzo siri ike, ọgwụgwọ nchekasị na ọgwụgwọ mwepụ hydrogen.
1) Na-akpachapụ anya.
Annealing bụ ikpo ọkụ nchara nke ihe owuwu ya na-esi na steeti nhata gaa na ọnọdụ okpomọkụ nke usoro ahụ ekpebiela, wee jiri nwayọọ nwayọọ mee ka ọ dị jụụ mgbe nchekwa ọkụ (na-ejikarị ọkụ ọkụ ma ọ bụ na-eli ozu na wayo) iji nweta usoro ọgwụgwọ okpomọkụ dị nso. nha nha ọnọdụ nke nhazi. Dị ka ihe mejupụtara ígwè ahụ si dị na nzube na ihe ndị a chọrọ nke ntanye, a na-ekewa annealing n'ime nkwụsị zuru ezu, nkwụsị nke isothermal, spheroidizing annealing, recrystallization annealing, annealing annealing na ihe ndị ọzọ.
(1) Mwepu zuru oke. Usoro izugbe nke nchacha zuru oke bụ: kpo oku nkedo nchara na 20 °C-30 Celsius C n'elu Ac3, na-ejide ya ruo oge ụfọdụ, nke mere na nhazi dị na ígwè ahụ na-agbanwe kpamkpam ka ọ bụrụ austenite, wee jiri nwayọọ nwayọọ na-ajụ oyi (na-emekarị. na-eme ka ọkụ dị jụụ) na 500 ℃- 600 ℃, na n'ikpeazụ jụrụ oyi na ikuku. Ihe a na-akpọ zuru ezu pụtara na a na-enweta ihe owuwu austenite zuru ezu mgbe ọ na-ekpo ọkụ.
Ebumnobi nke annealing zuru ezu na-agụnye: nke mbụ bụ imeziwanye usoro na-enweghị isi na nke na-enweghị isi nke ọrụ ọkụ na-akpata; nke abụọ bụ iji belata ike nke carbon ígwè na alloy ígwè nkedo n'elu ọkara carbon, si otú melite ha ọnwụ arụmọrụ (n'ozuzu, Mgbe hardness nke workpiece bụ n'etiti 170 HBW-230 HBW, ọ dị mfe bee. Mgbe hardness. dị elu ma ọ bụ dị ala karịa nke a, ọ ga-eme ka ịcha osisi sie ike); nke atọ bụ ikpochapụ nrụgide dị n'ime nke nkedo ígwè.
Ojiji nso nso annealing zuru ezu. Annealing zuru oke dabara adaba maka ihe nkedo carbon na alloy steel nwere ihe mejupụtara hypoeutectoid nwere ọdịnaya carbon sitere na 0.25% ruo 0.77%. Hypereutectoid ígwè ekwesịghị ikpochapụ kpamkpam, n'ihi na mgbe a na-ekpo ọkụ hypereutectoid n'elu Accm ma jiri nwayọọ nwayọọ mee ka ọ dị jụụ, cementite nke abụọ ga-agbanye n'akụkụ oke ọka austenite na ọdịdị netwọk, nke na-eme ka ike, plasticity na mmetụta siri ike nke ígwè ahụ dị ịrịba ama. daa.
(2) Isothermal Annealing. Isothermal annealing na-ezo aka na nkedo nchara kpo oku ruo 20 Celsius - 30 Celsius C n'elu Ac3 (ma ọ bụ Ac1), mgbe ejiri ya nwa oge, na-ajụ oyi ngwa ngwa ruo n'ogo kachasị elu nke usoro mgbanwe mgbanwe austenite austenite, wee jide ruo nwa oge. nke oge (mpaghara mgbanwe Pearlite). Mgbe austenite gbanwere ka ọ bụrụ pearlite, ọ na-ajụkwa nwayọọ nwayọọ.
(3) Ịkụnye Spheroidizing Annealing. Spheroidizing annealing bụ iji kpoo ihe nkedo nchara na okpomọkụ dị elu karịa Ac1, ma mgbe ogologo oge nke nchekwa ọkụ gasịrị, cementite nke abụọ dị na ígwè ahụ na-agbanwe ozugbo ghọọ granular (ma ọ bụ spherical) cementite, na mgbe ahụ na ngwa ngwa ọgwụgwọ okpomọkụ. usoro ajụkwa ka ụlọ okpomọkụ.
Ebumnuche nke spheroidizing annealing gụnyere: ibelata ike; na-eme ka ihe owuwu metallographic otu; imeziwanye arụmọrụ nke ịkpụ na ịkwado maka ịkwụsị.
Spheroidizing annealing bụ tumadi na eutectoid steels na hypereutectoid steels (carbon ọdịnaya karịrị 0.77%) dị ka carbon ngwá ọrụ ígwè, alloy spring steel, rolling bearing steel na alloy tool steel.
(4) mgbakasị ahụ mgbakasị ahụ na mgbakasị ahụ. A na-akpọkwa iwepụ ihe mgbakasị ahụ mgbakasị ahụ dị ala. Ọ bụ usoro nke nkedo ígwè na-ekpo ọkụ n'okpuru Ac1 okpomọkụ (400 °C - 500 Celsius C), wee debe ya ruo oge ụfọdụ, wee jiri nwayọọ nwayọọ mee ka ọ dị jụụ na ụlọ okpomọkụ. Ebumnuche nke mgbakasị ahụ mgbakasị ahụ bụ iwepụ nrụgide dị n'ime nke nkedo ahụ. Ọdịdị metallographic nke ígwè agaghị agbanwe n'oge usoro nkwụsịtụ nchekasị. A na-ejikarị annealing recrystallization iji kpochapụ usoro gbagọrọ agbagọ nke nhazi nrụrụ oyi na-akpata ma wepụ ike ọrụ. Okpomọkụ na-ekpo ọkụ maka recrystallization annealing bụ 150 °C - 250 Celsius n'elu okpomọkụ recrystallization. Mweghachi annealing recrystallization nwere ike megharia ọka kristal elongated ka ọ bụrụ kristal equiaxed edo mgbe nrụrụ oyi gasịrị, si otú ahụ na-ewepụ mmetụta nke ịrụsi ọrụ ike.
2) Normalizing
Normalizing bụ ọgwụgwọ okpomọkụ nke nchara na-ekpo ọkụ na 30 Celsius C - 50 Celsius C n'elu Ac3 (hypoeutectoid steel) na Acm (hypereutectoid steel), na mgbe oge nchekwa ọkụ gasịrị, a na-eme ka ọ dị jụụ na ụlọ okpomọkụ na ikuku ma ọ bụ na. mmanye ikuku. usoro. Normalizing na-enwe ngwa ngwa jụrụ oyi karia ntanye, ya mere nhazi a na-ahazi dị mma karịa usoro annealed, na ike ya na ike ya dịkwa elu karịa nke annealed. N'ihi obere mmepụta okirikiri na nnukwu akụrụngwa itinye n'ọrụ nke normalizing, a na-ejikarị eme ihe na nkedo ígwè dị iche iche.
E kewara ebumnobi nke normalization ụzọ atọ ndị a:
(1) Normalizing dị ka ọgwụgwọ okpomọkụ ikpeazụ
Maka nkedo ígwè nwere obere ike chọrọ, enwere ike iji normalizing dị ka ọgwụgwọ okpomọkụ ikpeazụ. Normalizing nwere ike nụchaa ọka, homogenize ihe owuwu, belata ferrite ọdịnaya na hypoeutectoid ígwè, na-abawanye na nụchaa pearlite ọdịnaya, si otú ahụ na-eme ka ike, ike na ike nke ígwè.
(2) Normalizing dị ka ọgwụgwọ tupu okpomọkụ
N'ihi na ígwè nkedo na ibu ngalaba, normalizing tupu quenching ma ọ bụ quenching na tempering (quenching na elu okpomọkụ tempering) nwere ike iwepụ Widmanstatten Ọdịdị na banded Ọdịdị, na-enweta a ezi na edo Ọdịdị. Maka cementite netwọk dị ugbu a na carbon steels na alloy tool steels nwere carbon ọdịnaya karịa 0.77%, normalizing nwere ike belata ọdịnaya nke cementite nke abụọ ma gbochie ya ịmepụta netwọkụ na-aga n'ihu, na-akwadebe nzukọ ahụ maka spheroidizing annealing.
(3) Melite arụmọrụ ịkpụ
Normalizing nwere ike melite arụmọrụ ịkpụ nke obere carbon ígwè. Isi ike nke ihe nkedo nchara carbon dị ala dị oke ala mgbe ọ gbasasịrị, ọ dịkwa mfe ịrapara na mma n'oge ịkpụ, na-ebute oke oke oke. Site n'ịhazi ọgwụgwọ okpomọkụ, ike nke nkedo ígwè dị ala nwere ike ịbawanye ruo 140 HBW - 190 HBW, nke dị nso na njedebe kachasị mma, si otú a na-eme ka arụmọrụ dị mma.
3) Nkwụsị
Quenching bụ usoro ọgwụgwọ okpomọkụ nke ihe nkedo ígwè na-ekpo ọkụ na okpomọkụ dị n'elu Ac3 ma ọ bụ Ac1, wee mee ka ọ dị jụụ ngwa ngwa mgbe ejiri ya ruo oge iji nweta nhazi martensitic zuru oke. Ihe nkedo nchara kwesịrị ịdị ọkụ n'oge ka nke kachasị dị ọkụ iji wepụ nrụgide na-ebelata ma nweta akụrụngwa akụrụngwa zuru oke achọrọ.
(1) Okpomọkụ na-emenyụ
The quenching kpo oku okpomọkụ nke hypoeutectoid ígwè bụ 30 ℃-50 ℃ n'elu Ac3; The quenching kpo oku okpomọkụ nke eutectoid ígwè na hypereutectoid ígwè bụ 30 ℃-50 ℃ n'elu Ac1. A na-ekpo ọkụ Hypoeutectoid carbon steel na okpomọkụ nke a kpọtụrụ aha n'elu iji nweta ezigbo ọka austenite, enwere ike nweta ezigbo usoro martensite mgbe emenyụchara. The eutectoid ígwè na hypereutectoid ígwè e spheroidized na annealed tupu quenching na kpo oku, ya mere, mgbe kpo oku ka 30 ℃-50 ℃ n'elu Ac1 na ezughị ezu austenitized, ihe owuwu bụ austenite na akụkụ undissed ezi-grained infiltration Carbon ahụ ahụ. Mgbe emenyụchara, austenite na-agbanwe ka ọ bụrụ martensite, a na-echekwa irighiri cementite a na-agbazeghị. N'ihi nnukwu ike nke cimentite, ọ bụghị nanị na ọ naghị ebelata ike nke ígwè, kamakwa ọ na-eme ka nkwụsị ya dịkwuo mma. Ọdịdị nkịtị emenyụ nke hypereutectoid ígwè bụ mma flaky martensite, na ezi granular cementite na obere ego nke austenite na-ejigide na-ekesa nke ọma na matriks. Ihe owuwu a nwere ike dị elu ma na-eyi nguzogide, mana ọ nwekwara ogo siri ike.
(2) Ngwọta dị jụụ maka ịmenyụ usoro ọgwụgwọ okpomọkụ
Ebumnuche nke quenching bụ iji nweta martensite zuru ezu. Ya mere, ọnụego nju oyi nke ígwè nkedo n'oge a na-emenyụ ga-adịrịrị karịa ọnụ ọgụgụ dị oke egwu nke igwe nkedo, ma ọ bụghị ya, enweghị ike ịnweta nhazi nke martensite na ihe ndị kwekọrọ. Agbanyeghị, oke jụrụ oyi nwere ike ibute nrụrụ ma ọ bụ mgbawa nke nkedo. Iji mezuo ihe ndị a chọrọ n'elu n'otu oge ahụ, a ga-ahọrọ usoro nju oyi kwesịrị ekwesị dị ka ihe nkedo ahụ si dị, ma ọ bụ usoro nke nhazi nhazi kwesịrị ịnakwere. Na okpomọkụ nso nke 650 ℃-400 ℃, ndị isothermal mgbanwe ọnụego nke supercooled austenite nke ígwè bụ ndị kasị ibu. Ya mere, mgbe nkedo agbanyụrụ, ekwesịrị ijide n'aka na ọ dị ngwa ngwa na oke okpomọkụ a. N'okpuru isi okwu Ms, ọnụego jụrụ oyi kwesịrị ịdị nwayọọ iji gbochie nrụrụ ma ọ bụ mgbawa. Igwe na-emenyụ ọkụ na-ejikarị mmiri, ngwọta mmiri ma ọ bụ mmanụ. N'ebe a na-emenyụ ogbo ma ọ bụ na-ekpo ọkụ, mgbasa ozi a na-ejikarị gụnyere mmanụ ọkụ, ọla a wụrụ awụ, nnu gbazere ma ọ bụ alkali gbazere.
The jụrụ ike nke mmiri na elu okpomọkụ mpaghara nke 650 ℃-550 ℃ bụ ike, na obi jụrụ ike nke mmiri na ala okpomọkụ mpaghara nke 300 ℃-200 ℃ bụ nnọọ ike. Mmiri na-adaba adaba maka imenyụ na iju oyi nke ihe nkedo carbon ígwè nwere ọdịdị dị mfe na nnukwu akụkụ obe. Mgbe a na-eji ya emenyụ na jụrụ oyi, mmiri na-ekpo ọkụ anaghị adị elu karịa 30 Celsius. Ya mere, a na-anabatakarị ya iji mee ka mgbasa mmiri sikwuo ike iji mee ka mmiri dị jụụ n'ime ebe kwesịrị ekwesị. Tụkwasị na nke ahụ, nnu na-ekpo ọkụ (NaCl) ma ọ bụ alkali (NaOH) na mmiri ga-eme ka ike dị jụụ nke ngwọta dịkwuo ukwuu.
The isi uru mmanụ dị ka a jụrụ ajụ bụ na jụrụ ọnụego na ala okpomọkụ mpaghara nke 300 ℃-200 ℃ bụ nnọọ ala karịa nke mmiri, nke nwere ike ukwuu ibelata esịtidem nchegbu nke quenched workpiece ma belata ohere nke deformation. na mgbawa nke nkedo. N'otu oge ahụ, ike jụrụ mmanụ na elu okpomọkụ nso nke 650 ℃-550 ℃ bụ dịtụ ala, nke bụkwa isi mwepu nke mmanụ dị ka a quenching ọkara. A na-achịkwa okpomọkụ nke mmanụ na-emenyụ ọkụ na 60 ℃-80 ℃. A na-ejikarị mmanụ emenyụ ihe nkedo ígwè alloy nwere ụdị dị mgbagwoju anya na imenyụ nkedo ígwè carbon na obere akụkụ obe na ụdị mgbagwoju anya.
Tụkwasị na nke ahụ, a na-ejikwa nnu gbazere eme ihe dị ka ihe na-emenyụ ọkụ, nke na-aghọ ịsa nnu n'oge a. A na-eji ebe ịsa mmiri dị elu mara nnu bat na ike jụrụ ya n'etiti mmiri na mmanụ. A na-ejikarị mmiri ịsa ahụ nnu mee ihe maka nkwụsịtụ na nkwụsị ogbo, yana maka ọgwụgwọ nkedo nke nwere ọdịdị dị mgbagwoju anya, obere akụkụ na nrụrụ siri ike chọrọ.
4) Iwe iwe
Tempering na-ezo aka na usoro ọgwụgwọ okpomọkụ nke ihe nkedo ígwè emenyụ ma ọ bụ nke a na-ahazi na-ekpo ọkụ na ọnọdụ okpomọkụ ahọrọ dị ala karịa ebe dị oké egwu Ac1, ma mgbe ọ nwụsịrị ruo oge ụfọdụ, a na-eme ka ha dị jụụ n'ogo kwesịrị ekwesị. Ngwọta okpomọkụ na-ekpo ọkụ nwere ike gbanwee usoro na-adịghị akwụ ụgwọ nke enwetara mgbe emechara ma ọ bụ mee ka ọ bụrụ ihe dị mma iji wepụ nchekasị ma melite plasticity na ike nke nkedo ígwè. N'ozuzu, usoro ọgwụgwọ okpomọkụ nke quenching na ọgwụgwọ okpomọkụ dị elu ka a na-akpọ ọgwụgwọ na-ekpo ọkụ. Ihe nkedo ígwè emenyụrịrị ga-adị ọkụ n'oge, na ihe nkedo ígwè emeziri kwesịrị ịdị ọkụ mgbe ọ dị mkpa. Ịrụ ọrụ nke nkedo ígwè mgbe iwe ọkụ na-adabere na okpomọkụ okpomọkụ, oge na ọnụ ọgụgụ nke oge. Mmụba nke ọnọdụ okpomọkụ na ịgbatị oge njide n'oge ọ bụla nwere ike ọ bụghị naanị belata nrụgide na-ebelata nke nkedo ígwè, kamakwa gbanwee martensite na-akwụghị ụgwọ ka ọ bụrụ martensite, troostite ma ọ bụ sorbite. A na-ebelata ike na ike nke nkedo ígwè, na plasticity na-emeziwanye nke ọma. Maka ụfọdụ steel alloy na alloying ọcha na-etolite carbide siri ike (dị ka chromium, molybdenum, vanadium na tungsten, wdg), ike na-abawanye na ike na-ebelata mgbe iwe na 400 ℃-500 ℃. A na-akpọ ihe omume a hardening nke abụọ, ya bụ, ike nke nkedo nkedo n'ime ọnọdụ ọkụ na-erute kacha. N'ime mmepụta n'ezie, ihe nkedo alloy nke ọkara nwere njirimara siri ike nke abụọ kwesịrị iwe ọkụ ọtụtụ oge.
(1) Ọnọdụ okpomọkụ dị ala
The okpomọkụ nso nke ala okpomọkụ tempering bụ 150 ℃-250 ℃. Obere okpomọkụ tempering nwere ike nweta tempered martensite Ọdịdị, nke a na-bụ-eji maka quenching elu carbon ígwè na quenching elu alloy ígwè. Tempered martensite na-ezo aka na nhazi nke cryptocrystalline martensite gbakwunyere ezigbo carbides granular. Ọdịdị nke hypoeutectoid ígwè mgbe obere okpomọkụ tempering na-ewe iwe martensite; Ọdịdị nke hypereutectoid ígwè mgbe ala okpomọkụ tempering bụ tempered martensite + carbides + nọgidere austenite. Ebumnuche nke iwe ọkụ dị ala bụ iji kwalite nchara siri ike nke ọma ka ọ na-edobe ike siri ike (58HRC-64HRC), ike dị elu ma na-eyi nguzogide, ebe ọ na-ebelata nrụgide nkwụsị na nhịkọ nke nkedo ígwè.
(2) Ọkpụkpọ okpomọkụ
The tempering okpomọkụ nke ọkara okpomọkụ bụ n'ozuzu n'etiti 350 ℃-500 ℃. Ọdịdị ahụ mgbe ọ na-ewe iwe na okpomọkụ nke ọkara bụ nnukwu ego nke cimentite dị mma gbasasịa ma kesaa na matriks ferrite, ya bụ, ihe owuwu troostite. Ferrite dị n'ụdị troostite na-ewe iwe ka na-ejigide ọdịdị nke martensite. A na-ekpochapụ nrụgide dị n'ime nke ihe nkedo ígwè mgbe a na-ewe iwe ọkụ, na ha nwere oke ngbanwe dị elu na njedebe mkpụrụ, ike dị elu na ike siri ike, na ezigbo plasticity na siri ike.
(3) Igwe ọkụ dị elu
The elu okpomọkụ tempering okpomọkụ bụ n'ozuzu 500C-650C, na okpomọkụ ọgwụgwọ usoro na-agwakọta quenching na ụdi elu okpomọkụ tempering a na-akpọkarị quenching na tempering ọgwụgwọ. Ọdịdị ahụ mgbe okpomọkụ dị elu na-ewe iwe sorbite, ya bụ, cimentite dị mma na ferrite. Ferrite dị na sorbite na-ewe iwe bụ polygonal ferrite nke na-enweta recrystallization. Ihe nkedo ígwè mgbe okpomọkụ dị elu nwere ezigbo ihe eji arụ ọrụ zuru oke n'ihe gbasara ike, plasticity na ike. A na-eji tempering dị elu mee ihe na ọkara carbon ígwè, ígwè alloy dị ala, na akụkụ dị iche iche dị mkpa dị mkpa nwere ike mgbagwoju anya.
5) Ọgwụgwọ siri ike
Ebumnuche bụ isi nke ọgwụgwọ ngwọta bụ ịgbari carbides ma ọ bụ usoro ndị ọzọ na-agbapụta n'ime ngwọta siri ike iji nweta usoro nhazi nke otu usoro. Nkedo nke austenitic igwe anaghị agba nchara, austenitic manganese ígwè na mmiri ozuzo siri ike igwe anaghị agba nchara kwesịrị n'ozuzu siri ike ngwọta na-emeso. Nhọrọ nke okpomọkụ ngwọta na-adabere na ihe mejupụtara kemịkalụ na eserese oge nke nchara nkedo. Okpomọkụ nke austenitic manganese ígwè nkedo bụ n'ozuzu 1000 ℃ - 1100 ℃; okpomọkụ nke austenitic chromium-nickel igwe anaghị agba nchara bụ n'ozuzu 1000 ℃-1250 ℃.
Ọdịnaya carbon nke dị na nkedo ígwè na-adị elu yana ihe ndị na-emepụta ihe na-adịghị edozi, otú ahụ ka okpomọkụ ngwọta ya siri ike kwesịrị ịdị elu. Maka mmiri ozuzo siri ike nkedo ígwè nwere ọla kọpa, ike nke nkedo nchara na-abawanye n'ihi mmiri ozuzo nke akụkụ ọla kọpa siri ike na steeti dị ka nkedo n'oge oyi. Iji mee ka nhazi ahụ dị nro ma melite arụmọrụ nhazi, ihe nkedo ígwè kwesịrị ka edozi ihe ngwọta siri ike. Ya siri ike ngwọta okpomọkụ bụ 900 ℃-950 ℃.
6) Ọgwụgwọ ike ike mmiri ozuzo
Ngwọta na-eme ka mmiri sie ike bụ ọgwụgwọ na-agbasasị ike nke a na-eme n'ime oke okpomọkụ, nke a makwaara dị ka ịka nká. Ihe kachasị mkpa nke ọgwụgwọ hardening mmiri ozuzo bụ na na okpomọkụ dị elu, carbides, nitrides, intermetallic compounds na ndị ọzọ na-adịghị akwụ ụgwọ n'etiti usoro na-precipitated si supersaturated siri ike ngwọta na chụsasịrị na matriks, si otú na-eme ka ígwè nkedo keukwu Mma n'ibu Njirimara na ike siri ike.
Ọnọdụ okpomọkụ nke ọgwụgwọ ịka nká na-emetụta kpọmkwem arụmọrụ ikpeazụ nke nkedo ígwè. Ọ bụrụ na okpomọkụ ịka nká dị ntakịrị, oge mmiri ozuzo na-eme ka ike sie ike ga-eji nwayọọ nwayọọ na-asọpụta; ọ bụrụ na okpomọkụ nke ịka nká dị elu, nchịkọta nke oge a na-eme ka ọ dị elu ga-eme ka ịka nká, na arụmọrụ kachasị mma agaghị enweta ya. Ya mere, ebe a na-emepụta ihe kwesịrị ịhọrọ ogo ịka nká kwesịrị ekwesị dịka ọkwa nchara nkedo na arụ ọrụ a kapịrị ọnụ nke nkedo ígwè. The ịka nká okpomọkụ nke austenitic okpomọkụ na-eguzogide nkedo ígwè bụ n'ozuzu 550 ℃-850 ℃; okpomọkụ nke ịka nká nke nnukwu mmiri ozuzo siri ike nkedo ígwè bụ n'ozuzu 500 ℃.
7) Ọgwụgwọ enyemaka nchekasị
Ebumnuche nke ọgwụgwọ okpomọkụ na-enye mgbakasị ahụ bụ iwepụ nrụgide nkedo, ịkwụsị nrụgide na nchekasị nke a na-emepụta site n'ịrụ ọrụ, iji mee ka nha nkedo ahụ guzosie ike. A na-ekpocha ọgwụgwọ okpomọkụ maka nchekasị ruo 100C-200C n'okpuru Ac1, wee debe ya ruo oge ụfọdụ, ma mesịa mee ka ọkụ dị jụụ. Ọdịdị nke nkedo ígwè agbanweghị n'oge usoro enyemaka nrụgide. Ihe nkedo ígwè carbon, ihe nkedo ígwè dị ala na ihe nkedo ígwè dị elu nwere ike ịnweta ọgwụgwọ enyemaka nrụgide.
4. Mmetụta ọgwụgwọ okpomọkụ na Njirimara nke nkedo ígwè
Na mgbakwunye na arụmọrụ nke nkedo ígwè na-adabere na nhazi nke kemịkalụ na usoro nkedo, a pụkwara iji usoro ọgwụgwọ okpomọkụ dị iche iche mee ka ọ nwee ihe nrụpụta ọrụ zuru oke. Ebumnuche n'ozuzu nke usoro ọgwụgwọ okpomọkụ bụ imeziwanye mma nke nkedo, belata ibu nke nkedo, ịgbatị ndụ ọrụ ma belata ụgwọ ọrụ. Ọgwụgwọ okpomọkụ bụ ụzọ dị mkpa iji melite akụrụngwa akụrụngwa nke nkedo; ihe eji arụ ọrụ nke nkedo bụ ihe ngosi dị mkpa maka ikpebi mmetụta ọgwụgwọ okpomọkụ. Na mgbakwunye na ihe ndị a na-esote, ebe a na-emepụta ihe ga-atụlekwa ihe ndị dị ka usoro nhazi, nkwụsị ọrụ na ihe eji achọ ihe nkedo mgbe ikpo ọkụ na-eme ka ọkpụkpụ ígwè.
1) Mmetụta nke ọgwụgwọ okpomọkụ na ike nke nkedo
N'okpuru ọnọdụ nke otu ihe nkedo ígwè, ike nke nkedo ígwè mgbe usoro ọgwụgwọ okpomọkụ dị iche iche na-enwe ọganihu. N'ikwu okwu n'ozuzu, ike nkwụsị nke nkedo ígwè carbon na nkedo ígwè dị ala nwere ike iru 414 Mpa-1724 MPa mgbe ọgwụgwọ okpomọkụ gasịrị.
2) Mmetụta ọgwụgwọ okpomọkụ na Plasticity nke nkedo ígwè
Usoro ihe nkedo nke ihe nkedo ígwè bụ nke siri ike na plasticity dị ala. Mgbe ọgwụgwọ okpomọkụ gasịrị, a ga-emeziwanye microstructure na plasticity ya. Karịsịa plasticity nke ihe nkedo ígwè mgbe quenching na tempering ọgwụgwọ (quenching + elu okpomọkụ tempering) ga-butere mma.
3) Ike nke nkedo ígwè
A na-enyochakarị ihe nrịbama siri ike nke nkedo ígwè site na nnwale mmetụta. Ebe ọ bụ na ike na ike nke nkedo ígwè bụ ụzọ abụọ na-emegiderịta onwe ha, ebe a na-ahụ maka ebe a na-emepụta ihe aghaghị ime echiche zuru oke iji họrọ usoro ọgwụgwọ okpomọkụ kwesịrị ekwesị iji nweta ihe nrụpụta ọrụ zuru oke nke ndị ahịa chọrọ.
4) Mmetụta ọgwụgwọ ikpo ọkụ na-esi ike nke nkedo
Mgbe ike nke igwe nkedo bụ otu ihe ahụ, ike nke nkedo nkedo mgbe ọgwụgwọ okpomọkụ gasịrị nwere ike igosipụta ike nke nkedo ahụ. Ya mere, a pụrụ iji isi ike mee ihe dị ka ihe nrịbama nke na-eme ka a na-eme ihe iji chọpụta ọrụ nke nkedo ígwè mgbe ọgwụgwọ okpomọkụ gasịrị. N'ikwu okwu n'ozuzu, isi ike nke ihe nkedo carbon nwere ike iru 120 HBW - 280 HBW mgbe ọgwụgwọ okpomọkụ gasịrị.
Oge nzipu: Jul-12-2021